Gillfab® 1050 is a general purpose laminate made from fiberglass cloth reinforced epoxy resin. Gillfab® 1050 is available with a peel ply on both sides for ensuring a bondable
surface. Gillfab® 1050 comes in sheet form.
此層壓板專為一般飛機用途而設計。
| Gillfab® 1050 (Sheet form) | |
| 厚度，英寸（毫米） | 0.020 (0.51) 可依要求提供其他厚度 |
| 長度，英寸（毫米） | 標準 144 (3,658) 最多 168 (4,267) |
| 寬度，英寸（毫米） | 標準 48 (1,219) 最多 60 (1,524) |
樹脂： 環氧樹脂
加強： 機織玻璃纖維布
以下測試是根據所示的 ASTM 進行的。
| TGC 部件號 | 1050 |
|---|---|
| 重量，psf (kg/m2) | 0.24 (1.2) |
| 拉伸強度，ksi (MPa) 翹曲 | 55 (380) |
| 拉伸強度，ksi (MPa) 填充 | 55 (380) |
| 吸水率，% | <1 |
| 60 秒垂直可燃性 | 經過 |
所示數字反映了典型值，不應用作設計規範。
根據 ASTM D-638，類型 1 進行張力測試。
Water Absorption per ASTM D570, dried one hour at 225°F followed by a 24 hour water soak.
當遵循推薦的預防措施時，本產品可以安全使用和應用。使用本產品前，請閱讀並理解 安全數據表 (SDS)，其中提供有關健康、身體和環境危害、處理預防措施和急救建議的信息。僅供工業使用。遠離兒童。可以在以下位置找到更多信息： www.thegillcorp.com.如需銷售和訂購信息，請致電 1-626-443-6094。
All recommendations, statements, values and technical data herein are based on tests The Gill Corporation believes to be reliable and correct, but accuracy and completeness of said tests are not guaranteed and are not to be construed as a warranty, either expressed or implied. Users shall rely on their own information and tests to determine suitability of the product for the intended use and assume all risks and liability resulting from their use of the product. The Gill Corporation’s sole responsibility shall be to replace that portion of the product that proves to be defective. The Gill Corporation will not be liable to the buyer or any third person for any injury, loss or damage directly or indirectly resulting from use of, or inability to use, the product. Recommendations or statements not contained in a written agreement signed by an officer of The Gill Corporation shall not be binding upon The Gill Corporation. Alcopan™, Alphex®, CGH® Dura-Core®, Gillfab®, Gillfloor®, Gilliner®, Gillite®, Gillfists®, GillVANA®, Higrid®, Hushgrid®, PAA-Core®, Plygrid®, Shapegrid®, Strikegrid®, Trussgrid® are registered trademarks of The Gill Corporation.