Gillfab® 1367


Gillfab® 1367 is a high strength, low FST grade liner constructed using a combination of woven E and/or S-glass cloth with a modified phenolic resin system and a 1 mil white polyvinyl fluoride film overlay on the face side for surface reflectivity and uniform appearance.


The cargo liner is designed for use in the cargo compartment, bulkhead facings, and blowout panels for aircraft.

Also used as backing material for non-textile floor mats used in wet areas of cabin interior (without polyvinyl fluoride film overlay).


  • High impact strength
  • Fire resistant
  • Corrosion resistant
  • Low moisture absorption
  • Low smoke and toxicity generation
  • Service temperature -40°F to 220°F (-40°C to 110°C)


Thickness, inch (mm)0.050 (1.27)
0.070 (1.78)
Length, inch (mm)Standard 144 (3,658)
Maximum 168 (4,267)
Width, inch (mm)Standard 48 (1,219)
Maximum 72 (1,829)
ColorFace side White Tedlar®
Back side Amber




  • Boeing BMS 8-223 Cl 2 Gr B, all types
  • McDonnell Douglas specification DMS 2419 Ty 50-90
  • LAC-C-22-1249 Cl 3
  • FAR Part 25 Appendix F Parts I and III (Burn Through)
  • ATS 1000.001

Alternative Gillfab® 1367 Products

Gillfab® 1367 series are high impact and fire resistant fiberglass reinforced phenolic laminates for aircraft cargo liner applications.

TGC Product No.Difference
Gillfab® 1367 Slightly higher impact values than 1367A, and offering additional thickness.
Gillfab® 1367AEconomical alternative to 1367 with standard weight and thickness requirements.
Gillfab® 1367BThinner and lighter than 1367A.
Gillfab® 1367C1367A in roll form.
Gillfab® 1367E1367A with 1 mil white polyvinyl fluoride film bonded to both faces of the laminate.
Gillfab® 1367F1367A molded to a “Z” shape for wire spacing in cargo bay.
Gillfab® 1367GExtremely thin, light weight and superior impact strength to corresponding types.
Gillfab® 1367M1367B in roll form.
Gillpatch® 1367PPatch laminate intended for repairing facings of 1367A.

Performance Properties, Typical

The following tests are run in accordance with BMS 8-223 specification requirements.

TGC Part Number1367-0501367-070
Thickness, inch (mm)0.051 (1.30)0.066 (1.67)
Weight, psf (kg/m2)0.47 (2.30)0.64 (3.12)
Impact Strength, ft-lbs (N-m)53 (71)59 (79)
Water Absorption, %1.31.0
Edge Bearing, ksi (MPa)Warp
42,000 (290)
40,000 (275)
47,000 (324)
45,000 (310)
FlammabilityMeets FAR 25.853 & 855 Appendix F Part I & III
Polyvinyl Fluoride Film Peel Separation, inch (mm)No Polyvinyl Fluoride Film Peel Separation

Figures shown reflect typical values and should not be used as design specifications.