Gillfab® 1367G



Gillfab® 1367G is an ultra-light weight, high strength, low FST liner constructed fromwoven S-glass cloth with a modified phenolic resin system and a 1 ml white polyvinyl fluoride film overlay on the face side. Gillfab® 1367G is an alternative toother Gillfab® 1367 series for aircraft cargo liners which maximizes weight savings.


Cargo liners for cargo compartment, bulkhead facings and blowout panels for aircraft.


  • Superior impact strength
  • Fire resistant
  • Corrosion resistant
  • Low moisture absorption
  • Low smoke and toxicity generation
  • Service temperature -40°F to 220°F (-40°C to 110°C)
  • Offers 30-40% weight savings as compared to Gillfab® 1367/1367A


Thickness, inch (mm)0.007 (0.178)0.027 (0.686)
Length, inch (mm)Standard 144 (3,658)Maximum 168 (4,267)
Width, inch (mm)Standard 48 (1,219)Maximum 60 (1,524)
ColorFace side1 mil White polyvinyl fluoride film
Back sideAmber




  • Boeing BMS 8-223, Class 5, Grade B, all types
  • FAR Part 25 Appendix F Parts I and III (Burn Through)

Alternative Gillfab® 1367 Products

Gillfab® 1367 series are high strength, high impact and fire resistant fiberglass reinforced phenolic laminates for aircraft cargo liner

TGC Product No.Difference
Gillfab® 1367Slightly higher impact values than 1367A, and offering additional thickness.
Gillfab® 1367AEconomical alternative to 1367 with standard weight and thickness requirements.
Gillfab® 1367BThinner and lighter than 1367A.
Gillfab® 1367C1367A in roll form.
Gillfab® 1367E1367A with 1mil white polyvinyl fluoride film bonding on both faces of the laminate.
Gillfab® 1367F1367A molded to a “Z” shape for wire spacing in cargo bay.
Gillfab® 1367GExtremely thin, lightweight and superior impact strength to corresponding types.
Gillfab® 1367M1367B in roll form.
Gillpatch® 1367PPatch laminate intend for repairing facings of 1367A.

Performance Properties, Typical

The following tests are run in accordance with BMS 8-223 specification requirements.

TGC Part Number1367G0071367G027
Thickness, inch (mm)0.007 (0.18)0.026 (0.69)
Weight, psf (kg/m2)0.067 (0.33)0.247 (1.20)
Impact Strength, ft-lbs (N-m)18 (24)39 (53)
Double Point Edge Bearing, lbs (N), maxWarp202 (898)N/A
Fill200 (890)N/A
FlammabilityMeet FAR 25.853 Appendix F Part I
Polyvinyl Fluoride Film Peel Separation, inchNo Polyvinyl Fluoride Film Peel Separation

Figures shown reflect typical values and should not be used as design specifications.