Gillfab® 1368G series laminates are ultra-light weight, high strength, low FST grade liners constructed using S-glass cloth with a modified phenolic resin system and an optional 1 mil white Polyvinyl Fluoride (PVF) film overlay on the face side for surface reflectivity and uniform appearance. Gillfab®1368G is an alternative to other Gillfab® 1368 series for aircraft cargo liners which maximizes weight savings.


Cargo liners for cargo compartment, bulkhead facings and blowout panels for aircraft.


  • High impact strength
  • Fire resistant
  • Corrosion resistant
  • Low moisture absorption
  • Low smoke and toxicity generation
  • Service temperature -40°F to 220°F (-40°C to 110°C)
  • Offers 30-40% weight savings as compared to Gillfab® 1368A


Gillfab® 1368G
1-Sided PVF Film
inch (mm)
0.007 (0.178)
0.027 (0.686)
LengthStandard 144 inch (3,658 mm)
Maximum 168 inch (4,267 mm)
WidthStandard 48 inch (1,219 mm)
Maximum 72 inch (1,829 mm)

SidesGillfab® 1368GAvailable Upon Request
ColorFace side1 mil White PVF FilmAmber
Granite Grey
Misty Beige
ColorFace sideAmberAmber


Reinforcement: Woven fiberglass cloth
Resin System: Phenolic
Surface Finish: 1 mil white PVF film overlay for standard applications


Gillfab® 1368G

  • Boeing BMS 8-223, Class 5, Grade B, Types 7 and 27
  •  CDM010-09 Class 5, Grade B
  • FAR Part 25 Appendix F Parts I and III (Burn Through)

Alternative Gillfab® 1368 Products

Gillfab® 1368 series are high strength, high impact and fire resistant fiberglass reinforced phenolic laminates for aircraft cargo liner applications.

TGC Product No.Difference
Gillfab® 1368AHigh strength, high impact, low FST, fiberglass reinforced phenolic laminate for aircraft cargo liner applications.
Gillfab® 1368BThinner and lighter than 1368A.
Gillfab® 1367C1368A construction in roll form.
Gillfab® 1368E1368A with 1mil white PVF film bonded to both faces of the laminate.
Gillfab® 1368GExtremely thin, lightweight and superior impact strength to corresponding types.
Gillfab® 1367M1368B construction in roll form.

Performance Properties, Typical

TGC Part Number1368G0071368G027
Thickness, inch (mm)0.007 (0.18)0.026 (0.69)
Weight, psf (kg/m2)0.067 (0.33)0.247 (1.20)
Impact Strength1, ft·lbf (N·m)13 (18)33 (45)
Edge Bearing2, kpsi (mpa)Warp
55 (379)
50 (345)
55 (379)
50 (345)
Climbing Drum Peel3, lbf/3 inch width (N/76 mm width)Warp
340 (1,510)
300 (1,330)
Double Point Edge Bearing2 lbf (N)Warp
315 (1,400)
300 (1,330)
Overlay Film PeelSup>4 lb/in (N/mm) 3.0 (0.52) – No PVF Film Separation3.0 (0.52) – No PVF Film Separation
FlammabilityMeets requirements of FAR 25.853 & 855 Appendix F Part I & III

Figures shown reflect typical values and should not be used as design specifications.
1 – Calculated per ASTM D5420 using a modified dart and specimen test frame.
2 – Tested per ASTM D953 using a modified test fixture.
3 – Tested per ASTM D1781.
4 – Tested using a modified ASTM D3330 using a standard tape to peel PVF film overlay.