Gilliner® 1366/1366T

Gilliner 1366T image

Overview

Gilliner® 1366 and 1366T are high impact resistant grade liners constructed of woven E- and S-glass cloth with a polyester resin system to optimize strength, weight and cost. This product offers superior mechanical properties and higher strength-to-weight ratio compared to all E glass constructions. 1 mil. white polyvinyl fluoride film overlay on the face side is included for Gilliner® 1366T.

Applications

Aircraft cargo compartment liner for general purpose use.

Features

  • High impact strength
  • Abrasion resistant
  • Corrosion resistant
  • Fire resistant

Availability

Sheet Form Roll Form
Thickness, inch (mm) 0.011 (0.28)
0.020 (0.51)
0.030 (0.76)
0.040 (1.02)
0.045 (1.14)
0.050 (1.27)
0.060 (1.52)
0.070 (1.78)
0.090 (2.29)
0.011 (0.28)
0.020 (0.51)
0.030 (0.76)
0.040 (1.02)
0.045 (1.14)
0.050 (1.27)
LengthTypical 144 inch (3,658 mm)
Maximum 168 inch (4,267 mm)
Typical 150 feet (45,720 mm)
WidthTypical 48 inch (1,219 mm)
Maximum 72 inch (1,829 mm)
Typical 48 inch (1,219 mm)
Maximum 60 inch (1,524 mm)
ColorNatural or White

Construction

Resin: Polyester

Reinforcement: Woven E- and S-glass fiber cloth

Surface: 1 mil. white polyvinyl fluoride film overlay (for 1366T)

Specifications

  • DHMS P1.42, Class B Grade 1 and Grade 2
  • FAR Part 25 Appendix F Parts I and III (burn through)

Performance Properties, Typical

TGC Part Number1366-0111366-0201366-0301366-0401366-0451366-070
Thickness, inch (mm)0.011 (0.28)0.020 (0.51)0.030 (0.76)0.040 (1.02)0.045 (1.14)0.070 (1.78)
Weight, psf (kg/m2)0.12 (0.59)0.18 (0.88)0.30 (1.46)0.38 (1.86)0.43 (2.10)0.71 (3.47)
Tensile Strength1, ksi (MPa) Warp66 (455)68 (469)61 (421)95 (655)57 (393)63 (434)
Fill56 (386)51 (352)79 (545)53 (365)60 (414)
Water Absorption2 , % Increase1.0
Abrasion Resistance3 , g/1000 cycles0.1
Impact Strength4 , ft-lb (N-m)13 (18)16 (22)20 (27)25 (34)32 (43)47 (64)
Edge Bearing Strength5, ksi (MPa)Warp45 (200)
Fill
Flexural Strength6, ksi (MPa) WarpN/A 56 (386)32 (221)35 (241)
Fill53 (365)30 (207)32 (221)
Flexural Tangent Modulus6, Msi (GPa) WarpN/A3.0 (21)2.9 (20)3.4 (23)
Fill2.2 (15)2.5 (17)
FlammabilityMeets FAR 25.853 & 855 Appendix F Part I & III

Table shown reflects typical values and should not be used as design specifications.
1 Tensile Strength was tested and calculated per ASTM D638.
2 Water Absorption was tested and calculated per ASTM D570.
3 Abrasion resistance was tested per ASTM D3389 with CS-10 Wheel, 500 grams of weight, and minor modifications
to specimen preparation.
4 Impact Strength was tested calculated per ASTM D5420 using a modified dart and specimen test frame.
5 Edge Bearing Strength was calculated per ASTM D953 using a modified tension loading fixture.
6 Flexural Strength and Modulus were tested and calculated per ASTM D790.