Gilliner® 1568A is a high wear resistant liner constructed from woven E-glass cloth with a polyester resin system. This product features resin rich surfaces to address wear through over frame sections and attach points that are associated with repetitive bulk cargo loading.
Cargo liners for cargo compartment, bulkhead facing for aircraft. Designed for lower sidewalls where in-service conditions may result in wear through over frame sections, impact damage and/or fastener hole tear out at attach points.
|Sheet Form||Roll Form|
|Thickness, inch (mm)||0.020 (0.51)|
|Length||Typical 144 inch (3,658 mm)||Typical 150 feet (45,720 mm)|
|Width||Typical 48 inch (1,219 mm)|
Maximum 72 inch (1,829 mm)
|Typical 48 inch (1,219 mm)
Maximum 60 inch (1,524 mm)
Reinforcement: Woven E-glass fiber cloth
Surface: Non-woven adhesive carrier for high wear resistant applications
|TGC Part Number||1568A020||1568A045|
|Thickness, inch (mm)||0.020 (0.51)||0.045 (1.14)|
|Weight, psf (kg/m 2 )||0.20 (1.03)||0.46 (2.44)|
|Tensile Strength1, ksi (MPa)||Warp||74 (510)||70 (483)
|Fill||64 (441)||54 (372)|
|Water Absorption2, % Increase||0.5||0.5|
|Impact Strength3, ft-lb (N-m)||11 (15)||23 (31)|
|Edge Bearing Strength4,||Warp||50 (345)||38 (262)
|Fill||43 (296)||35 (241)|
|Flexural Strength5, ksi (MPa)||Warp||N/A||46 (317)|
|Flexural Tangent Modulus5, Msi (GPa)||Warp||N/A||2.6 (18)|
|Flammability||Meets FAR 25.853 & 855 Appendix F Part I & III|
Table shown reflects typical values and should not be used as design specifications.
1Tensile Strength was tested and calculated per ASTM D638.
2Water Absorption was tested and calculated per ASTM D570.
3Impact Strength was tested calculated per ASTM D5420 using a modified dart and specimen test frame.
4Edge Bearing Strength was calculated per ASTM D953 using a modified tension loading fixture.
5Flexural Strength and Modulus were tested and calculated per ASTM D790.